Stainless Steels Manual Electrode E310-15 fanadiovana petrochemical sy electrode fampidirana simika
TECHNOLOGY WELD
Aza avela ny fanontaniana
Manohy manenjika anao
Arc instability
Famolavolana tsy mendrika
Mifofofofo be loatra
Mety amin'ny vokatra avo lenta amin'ny hafanana
toy ny lafaoro avo lenta, fitaovana fanodinana arintany,
azo ampiasaina amin'ny welding fitaovana tsy mitovy.
Low hydrogène madio austenitic stainless vy
tanana electrode, ny tena composition dia 25% Cr-20% Ni.
Ripple tsara
Marin-toerana ambony hafanana fampisehoana,
azo ampiasaina hatramin'ny 1150C tontolo iainana
Fahombiazana welding tsara, fanoherana afo tsara,
porosity tsara fanoherana, toetra mekanika miorina amin'ny metaly mitsonika.
Mora slagging
Parameter vokatra
COMPONET CHEMIKA:
| FITIAVANA (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | hafa |
| GB/T RATSY | 0.102 | 1.66 | 0.4 | 0.27 | 0,005 | 21.8 | 25.6 | 0.06 | 0.10 | - |
FANANANA MEKANIKA:
| NY FANANANA | HERINANDRO (MPa) | HERIN'NY FANITATRA (MPa) | IMPACT VALUE J/℃ | Fitsaboana hafanana °C*h | ||||
| GB/T RATSY | 595 | 34 | - | - | ||||
PARAMETER WELD RECOMMENDED:
| SPECIFICATIONS DIAMETERS (mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
| HERINATRATRA (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||
Fanohanana orinasa
Ny vokatra dia mety amin'ny a
be dia be ny fampiharana
TECHNOLOGY WELD
Harbin elektrika
vavahady telo CMT
-
CJ50
jack-up drill
-
Xinjiang Kela 2 Central
tetikasa toeram-pitsaboana
COMPONET CHEMIKA:
| FITIAVANA (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | hafa |
| GB/T RATSY | 0.102 | 1.66 | 0.4 | 0.27 | 0,005 | 21.8 | 25.6 | 0.06 | 0.10 | - |
FANANANA MEKANIKA:
| NY FANANANA | HERINANDRO (MPa) | HERIN'NY FANITATRA (MPa) | IMPACT VALUE J/℃ | Fitsaboana hafanana °C*h | ||||
| GB/T RATSY | 595 | 34 | - | - | ||||
PARAMETER WELD RECOMMENDED:
| SPECIFICATIONS DIAMETERS (mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
| HERINATRATRA (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||