Stainless Steels Manual Electrode E312-17 lasantsy sambo
TECHNOLOGY WELD
Aza avela ny fanontaniana
Manohy manenjika anao
Arc instability
Famolavolana tsy mendrika
Mifofofofo be loatra
Mety amin'ny karazana fitaovana vy mafy sy mafy
vy firaka izay sarotra ny welding sy mora triatra na manana porosity
Acid karazana roa-dingana Stainless vy tanana electrode, jet Arc,
Ny singa fototra dia 29% Cr-9% Ni, fantatra amin'ny anarana hoe "electrode universel.
Ripple tsara
Fampiasana welding tsara, arc stable, endrika tsara tarehy,
ripple marefo, mitsimoka kely, manala tavy mora.
Ny coating dia manana fanoherana afo tsara, fanoherana porosity tsara, ary toetra mekanika maharitra amin'ny metaly mitambatra
Mora slagging
Parameter vokatra
COMPONET CHEMIKA:
| FITIAVANA (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | hafa |
| GB/T RATSY | 0.057 | 1.1 | 0.74 | 0.026 | 0,005 | 9.8 | 28.4 | 0.07 | 0.11 | - |
FANANANA MEKANIKA:
| NY FANANANA | HERINANDRO (MPa) | HERIN'NY FANITATRA (MPa) | IMPACT VALUE J/℃ | Fitsaboana hafanana °C*h | ||||
| GB/T RATSY | 800 | 25 | - | - | ||||
PARAMETER WELD RECOMMENDED:
| SPECIFICATIONS DIAMETERS (mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
| HERINATRATRA (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||
Fanohanana orinasa
Ny vokatra dia mety amin'ny a
be dia be ny fampiharana
TECHNOLOGY WELD
-
2,3 tapitrisa barika
SBM Fast4ward FPSO
-
GDS-2209/GXS-E330
toerana misy fantsona fantsona
Hainan Huasheng
tilikambo fanarenana phenol
COMPONET CHEMIKA:
| FITIAVANA (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | hafa |
| GB/T RATSY | 0.057 | 1.1 | 0.74 | 0.026 | 0,005 | 9.8 | 28.4 | 0.07 | 0.11 | - |
FANANANA MEKANIKA:
| NY FANANANA | HERINANDRO (MPa) | HERIN'NY FANITATRA (MPa) | IMPACT VALUE J/℃ | Fitsaboana hafanana °C*h | ||||
| GB/T RATSY | 800 | 25 | - | - | ||||
PARAMETER WELD RECOMMENDED:
| SPECIFICATIONS DIAMETERS (mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
| HERINATRATRA (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||