TIG Welding Wire Ho an'ny Stainless Steel ER410NM Container welding akora
TECHNOLOGY WELD
Aza avela ny fanontaniana
Manohy manenjika anao
Arc instability
Famolavolana tsy mendrika
Mifofofofo be loatra
Ampiasaina matetika amin'ny toby famokarana herinaratra sy valva
ary fotoana hafa mahatohitra sy mahatanty harafesina
Toy ny fanariana ASTM CA6NM na fitaovana mitovy amin'izany, famaritana kely 410, 410S, 405 ary fitaovana fototra hafa.
Ripple tsara
Noho ny fanampian'ny Ni sy Mo, ny tanjany sy ny hamafin'ny
avo kokoa noho ny 410 noho ny fitakiana fitakiana sy ny fanoherana ny harafesina
Arc marin-toerana, endrika tsara tarehy, miaraka amin'ny fahombiazan'ny fizotran'ny welding
Mora slagging
Parameter vokatra
COMPONET CHEMIKA:
| FITIAVANA (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | hafa |
| GB/T RATSY | 0.013 | 0.52 | 0.78 | 0.017 | 0.01 | 4.82 | 12.27 | 0.67 | - |
FANANANA MEKANIKA:
| NY FANANANA | HERINANDRO (MPa) | HERIN'NY FANITATRA (MPa) | Elongation/% | IMPACT VALUE J/℃ | Fitsaboana hafanana °C*h | |||||
| GB/T RATSY | - | 935 | 21 | 119/0 | 600*3 | |||||
Fanohanana orinasa
Ny vokatra dia mety amin'ny a
be dia be ny fampiharana
TECHNOLOGY WELD
-
85.000 m3 Tena lehibe
Ethane Ethylene Carrier (VLEC)
-
Guangxi Huayi
tilikambo manafoana methanol
-
Shaanxi Pucheng -50 ℃
propane spherical tank project
COMPONET CHEMIKA:
| FITIAVANA (wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | hafa |
| GB/T RATSY | 0.013 | 0.52 | 0.78 | 0.017 | 0.01 | 4.82 | 12.27 | 0.67 | - |
FANANANA MEKANIKA:
| NY FANANANA | HERINANDRO (MPa) | HERIN'NY FANITATRA (MPa) | Elongation/% | IMPACT VALUE J/℃ | Fitsaboana hafanana °C*h | |||||
| GB/T RATSY | - | 935 | 21 | 119/0 | 600*3 | |||||
-
Stainless steels Manual electrode E316L-16 weld ...
-
MIG Welding Wire Ho an'ny Stainless Steel ER309L 600...
-
Stainless steels Manual electrode E308-15 petro...
-
Stainless steels Manual electrode E410-16 weld ...
-
Stainless vy Flux cored tariby E308LT1-1 Weld ...
-
Stainless steels Flux cored tariby EGT1-1 Welding ...