Stainless vy Electrode manual E308-16 metaly fifandraisana data
TECHNOLOGY WELD
Aza avela ny fanontaniana
Manohy manenjika anao
Arc instability
Famolavolana tsy mendrika
Mifofofofo be loatra
Karazana calcium titanium
Stainless vy tanana electrode
Ny singa fototra dia 18% Cr- 9% Ni
Ripple tsara
Toetra mekanika maharitra
Avo ny taham-pahafahana X-Ray
Fampiharana isan-karazany
Mora slagging
Paramètre vokatra
COMPONET CHEMIKA:
FITIAVANA (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T RATSY | 0.08 | 0.5-2.5 | 1.00 | 180.-21.0 | 9.0-11.0 | 0.75 | 0.04 | 0.03 | 0.75 |
AWS RULES | 0.08 | 0.5-2.5 | 1.00 | 180.-21.0 | 9.0-11.0 | 0.75 | 0.04 | 0.03 | 0.75 |
VALUE OHATRA | 0.039 | 0.98 | 0.75 | 19.8 | 9.4 | 0.01 | 0.028 | 0,004 | 0.05 |
FANANANA MEKANIKA:
NY FANANANA | HERINANDRO (MPa) | HERIN'NY FANITATRA (MPa) | FANAMAFANA ℃ xh | IMPACT VALUE J/℃ | ELONGATION(%) | |||||
GB/T RATSY | - | 550 | - | - | 30 | |||||
AWS RULES | - | 550 | - | - | 30 | |||||
VALUE OHATRA | - | 605 | - | - | 43 |
PARAMETER WELD RECOMMENDED:
SPECIFICATIONS DIAMETERS (mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
HERINATRATRA (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 |
Fanohanana orinasa
Ny vokatra dia mety amin'ny a
be dia be ny fampiharana
TECHNOLOGY WELD
COMPONET CHEMIKA:
FITIAVANA (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T RATSY | 0.08 | 0.5-2.5 | 1.00 | 180.-21.0 | 9.0-11.0 | 0.75 | 0.04 | 0.03 | 0.75 |
AWS RULES | 0.08 | 0.5-2.5 | 1.00 | 180.-21.0 | 9.0-11.0 | 0.75 | 0.04 | 0.03 | 0.75 |
VALUE OHATRA | 0.039 | 0.98 | 0.75 | 19.8 | 9.4 | 0.01 | 0.028 | 0,004 | 0.05 |
FANANANA MEKANIKA:
NY FANANANA | HERINANDRO (MPa) | HERIN'NY FANITATRA (MPa) | FANAMAFANA ℃ xh | IMPACT VALUE J/℃ | ELONGATION(%) | |||||
GB/T RATSY | - | 550 | - | - | 30 | |||||
AWS RULES | - | 550 | - | - | 30 | |||||
VALUE OHATRA | - | 605 | - | - | 43 |
PARAMETER WELD RECOMMENDED:
SPECIFICATIONS DIAMETERS (mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
HERINATRATRA (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 |