Stainless vy tariby vita amin'ny metaly EC439 Welding Accessories

Stainless steels Metal cored tariby EC439 Welding Accessories Sary nasongadina

GB/T17853 TS 430-MM 12 0

AWS A5.22 EC439

A5.22M EC439

ISO 17633-B:TS 430-MM 12 0

Whatapp:+8613252436578

E-mail: sale@welding-honest.com

marika:JINGLEI

Modely:GCS-439Ti

Polarity famatsiana herinaratra:DC+

niaviany:CHINE

Mifanaraka amin'ny:Stainless vy

Habe:1.2mm

MOQ: 1T fahafahana:500T Isam-bolana

Fandoavana:TT,LC

OEM:Afaka mpanjifa

Alefaso mailaka aminay

Product Detail

famaritana

Tags vokatra

Fampiharana

Mety amin'ny rafitra setroka fiara sy fiara muffler welding.

COMPONET CHEMIKA:

FITIAVANA (wt%)	C	Mn	Si	Cr	Ni	Mo	P	S	Ti
GB/T RATSY	0.10	0.60	0.50	15.5-18.0	0.60	0.75	0.03	0.03	-
AWS RULES	0.04	0.80	0.80	17.0-19.0	0.60	0.50	0.03	0.03	10*C-1.1
VALUE OHATRA	0.025	0.55	0.48	17.9	0.01	0.01	0.008	0.010	0.41

FANANANA MEKANIKA:

NY FANANANA	HERINANDRO (MPa)	HERIN'NY FANITATRA (MPa)	IMPACT VALUE J/℃	ELONGATION(%)
GB/T RATSY	-	450	-	15
AWS RULES	-	-	-	-
VALUE OHATRA	-	480	-	20

PARAMETER WELD RECOMMENDED:

SPECIFICATIONS DIAMETERS (mm)		1.2
Volt		17-32
DIEM		120-280
halavan'ny fanitarana maina (mm)		15-20
Fikoriana entona (l/min)		15-25

Mampiavaka

Ny metaly weld dia misy singa Ti araka ny tokony ho izy ary manana oxidation tsara sy fanoherana ny harafesina.

Ny fametahana lamba manify dia tsy mora ny mandoro.

Ny arc dia malefaka sy marin-toerana, tsy dia misy splash, endrika tsara tarehy, saika tsy misy slag, famahanana tariby tsy miovaova ary fampihetseham-batana tsara.

Asehoy ny antsipiriany

Malemilemy sy miorim-paka miaraka amin'ny tifitra kely

Tsara endrika, saika tsy misy slag

Momba anay

Fampisehoana fioor orinasa

Raharaha fampiharana

Hainan Huasheng phenol recovery tilikambo

2,3 tapitrisa barika SBM Fast4ward FPSO

Ny tena fitifirana orinasa

COMPONET CHEMIKA:

FITIAVANA (wt%)	C	Mn	Si	Cr	Ni	Mo	P	S	Ti
GB/T RATSY	0.10	0.60	0.50	15.5-18.0	0.60	0.75	0.03	0.03	-
AWS RULES	0.04	0.80	0.80	17.0-19.0	0.60	0.50	0.03	0.03	10*C-1.1
VALUE OHATRA	0.025	0.55	0.48	17.9	0.01	0.01	0.008	0.010	0.41